High Density 88/12 Tungsten Carbide Cobalt

CT2121-2

CT2121-2 is a Tungsten Carbide Cobalt coating applied using the HVOF process. The coating is very dense, very hard, very well bonded and suitable for use in the most aggressive wear environments. CT2121-2 is especially effective in applications where the component is exposed to abrasive media. Use up to 1,000ºF.

Typical Properties

Nominal Composition:
88% WC – 12% Co
Bond Strength:
In excess of 10,000 psi
Coating Porosity:
Less than 1%
Coating Hardness:
Vickers 1150-1350
As-sprayed Surface Roughness:
90-120 Ra

For the Following Applications:

CT2121-2 is used for severe service conditions of abrasive wear, hard surface wear, low temperature erosion and fretting. Typical components coated with this coating are steel mill rolls, paper mill rolls, corrugating rolls, pulp pumps, slurry pumps, concrete block manufacturing wear parts, etc.

Finishing

Finish CT2121-2 by diamond grinding. Flood cool with 2% oil solution. For roughing use 150 grit diamond wheels, work rotation should be 400 SFPM, .080” per pass crossfeed, .0005” per pass infeed. Finish with 400 grit diamond wheels, work rotation should be 400 SFPM, .040” per pass crossfeed, .0005” per pass infeed.

Finishes of 2-4 Ra are possible by grinding. This coating may also be superfinished to a 1 Ra finish.

Specifications

CT2121-2 meets the following specifications:

Want to learn more about CTS’ capabilities and thermal coating solutions?

Contact us today to consult directly with one of our representatives or certified engineers and discover how we can help you attain efficiency, productivity, and protection within 24 hours.