Alumina Zirconia


CT1100-1 is an Alumina Zirconia coating applied using the plasma spray process. The coating is chemically inert, stable at elevated temperatures, and resistant to stresses induced by thermal cycling. CT1100-1 is especially effective in applications where the component is exposed to certain molten metals. Use up to 1600º F.

Typical Properties

Nominal Composition
75% Al2O3 – 25% ZrO
Bond Strength
> 5,000 psi
Coating Porosity:
As-sprayed Surface Roughness
300-500 Ra

For the Following Applications:

CT1100-1 is used for severe service conditions of molten metal erosion. Typical components coated with this coating are steel mill galvanizing and aluminizing rolls.


Coatings of CT1100-1 are typically used as sprayed with no further finishing.


CT1100-1 meets the following specifications:

Internal CTS specifications only

Want to learn more about CTS’ capabilities and thermal coating solutions?

Contact us today to consult directly with one of our representatives or certified engineers and discover how we can help you attain efficiency, productivity, and protection within 24 hours.